Zirconia-alumina multiphase ceramic fibers with exceptional thermal stability by melt-spinning from solid ceramic precursor

Zirconia-alumina multiphase ceramic fibers with 80 wt% (Z80A20 fiber) and 10 wt% (Z10A90 fiber) proportions of zirconia were prepared via melt-spinning and calcination from solid ceramic precursors synthesized by controllable hydrolysis of metallorganics. The zirconia-alumina multiphase fibers had a diameter of about 10 µm and were evenly distributed with alumina and zirconia grains. The Z80A20 and Z10A90 ceramic fibers had the highest filament tensile strength of 1.78 GPa and 1.87 GPa, respectively, with a peak value of 2.62 GPa and 2.71 GPa. The Z80A20 ceramic fiber has superior thermal stability compared to the Z10A90 ceramic fiber and a higher rate of filament strength retention due to the stability in grain size. After heat treatment at 1100 °C, 1200 °C, and 1300 °C for 1 h respectively, the filament tensile strength retention rate of Z80A20 ceramic fibers was 87 %, 80 %, and 40 %. While Z10A90 ceramic fiber was fragile after being heated at 1300 °C. The results showed that the high zirconia content facilitated the fiber's thermal stability.     

Revisiting the Parallel Strategy for DOACROSS Loops

Journal of Computer Science and Technology - DOACROSS loops are significant parts in many important scientific and engineering applications, which are generally exploited pipeline/wave-front...     

An experimental study on the spray characteristics of pressure nozzle in a fluid bed granulation

The particles with a narrow size distribution are proper products in a fluid bed granulation and coating. As well, the process efficiency is one of the most important parameters, and the wall deposition of sprayed liquid reduces it. The modality of spray volume distribution is a key parameter in the definition of particle size distribution and process efficiency. This work is done in two steps: In the first step, an experimental study on spray characteristics including spray flux distribution, spray cone angle, and discharge coefficient is conducted. Based on the experimental data, the curves of liquid volume flux versus nozzle pressure and height are obtained. The results indicate that the flux distribution changes significantly with even small pressure and height changes. In the second step, the granulation process is carried out in a semi-industrial conical fluid bed, and the particles size distribution curves and the deposited mass on the bed wall are obtained. The results show that the precise determination of the spray flux distribution is an appropriate way to predict the well-advised nozzle pressure/height in order to achieve the narrow particle size distribution and high efficiency of the process.     

Optimal data-based binning for histograms and histogram-based probability density models

Histograms are convenient non-parametric density estimators, which continue to be used ubiquitously. Summary quantities estimated from histogram-based probability density models depend on the choice of the number of bins. We introduce a straightforward data-based method of determining the optimal number of bins in a uniform bin-width histogram. By assigning a multinomial likelihood and a non-informative prior, we derive the posterior probability for the number of bins in a piecewise-constant density model given the data. In addition, we estimate the mean and standard deviations of the resulting bin heights, examine the effects of small sample sizes and digitized data, and demonstrate the application to multi-dimensional histograms.     

Ultrashort pulse-induced elastodynamics in polycrystalline materials. Part I: Model validation

The coupled thermal-mechanical response of a polycrystalline metallic film in response to ultrafast optical impingement is investigated. The thermo-elastodynamics formulated in the article considers laser absorption along the axial direction and thermal diffusion along the radial direction to account for the normal and shear stresses initiated by the rapid heating. The generalized formulation incorporates a two-step hyperbolic temperature model that characterizes the energy transport of electrons and lattices as finite in velocity. The coupling of thermal and mechanical fields is established through considering the energy dissipated in the form of propagating thermo-mechanical disturbances. The thermo-elastodynamical response of the polycrystalline film is found to be a strong function of the electron heat capacity that is also temperature-dependent. In addition, grain size effects due to film surface and grain-boundary scatterings are found to impact several thermophysical properties of the material. The impact of the energy transport of electrons is particularly prominent when the thickness becomes comparable with the electron mean-free-path. A staggered-grid finite difference scheme is followed to simultaneously resolve the coupled thermo-elastodynamical responses using an axisymmetric model. The time variation of the normalized electron temperature of a single crystalline gold film derived from the generalized model is favorably examined against published physical data, thus demonstrating the feasibility of the formulation in depicting the electron transport dynamics in response to non-ablating ultrafast irradiation.     

基于神经网络算法的井下裂缝诊断与堵漏技术

在钻井过程中，常常钻遇不同宽度的井下地层裂缝。钻遇裂缝时容易发生钻井液漏失现象，甚至发生钻井液失返现象，严重影响了安全、高效钻井。目前裂缝封堵的方法常存在封堵成功率不高、堵漏承压能力低的问题，其中一个重要的原因是对井下地层的裂缝宽度等特征认识不清。基于地层裂缝产生的岩石力学机理，确定影响裂缝宽度关键的6个力学和工程因素，并利用神经网络计算的非线性、大数据特点建立了井下地层裂缝宽度的分析模型，模型包含输入层、输出层和3个隐藏层。通过该模型诊断井下裂缝宽度，提高了计算精度，平均误差仅为2.09%，最大误差为5.88%，解决钻井现场仅凭经验判断裂缝误差较大和依靠成像测井成本较高的问题。同时根据神经网络模型诊断得到的裂缝宽度优化堵漏材料的粒径配比，提高了裂缝内的架桥封堵强度和架桥的稳定性，封堵层的承压能力达到12.8 MPa，反向承压能力达到4.5 MPa。现场堵漏试验最高憋压10 MPa，经过封堵作业后大排量循环不漏，达到了裂缝性地层高效堵漏的目的，堵漏一次成功。      

悬浮法PVC树脂粒径的影响因素

讨论了悬浮法PVC树脂生产过程中影响树脂粒径的主要因素,有针对性地从聚合釜搅拌、反应配方、体系氧含量、pH值、聚合温度和转化率等方面提出了粒径的控制方案。     

某高硫铜硫矿工艺矿物学研究

研究了某高硫铜硫矿的工艺矿物学。结果表明,原矿中铜品位为2.85%,硫品位为24.32%,金含量为0.48g/t,铜、硫、金是主要回收的元素。原矿中的金属矿物有黄铜矿、黄铁矿、蓝辉铜矿。目的矿物黄铜矿和黄铁矿的嵌布粒度差异较大,且铜矿单体解离度相对较差。在选择工艺流程时应该注重氧化铜矿物的回收,同时要选择合适的磨矿细度,保证目的矿物单体解离。     

Precipitation location of secondary phase and microstructural evolution during static recrystallization of as-cast Ti-25V-15Cr-0.3Si titanium alloy

The microstructural evolution and precipitation location of the secondary phase of an as-cast Ti-25V-15Cr-0.3Si titanium alloy were investigated via isothermal compression experiments and heat treatment. The average aspect (length-to-width) ratio, average area and size of the grains at different heat treatment temperatures and holding time were analyzed and the effects of deformation and annealing time on the grain area and size were considered. It was found that the grain size was strongly influenced by the height reduction and holding time. Grain growth was significant when annealing time increased from 10 min to 2 h at 950 °C and height reduction of 30%; however, grain growth was minimal at annealing time between 2 and 4 h. Many dispersion particles were observed to form in continuous chains; the precipitation location was confirmed to be along initial grain boundaries, and the dispersion particles were identified to be Ti₅Si₃ phase by TEM.